Comparative Study on Bending Strength of Metallic Bone Staple

  • Authors

    • Nur Hidayatul Nadhirah Elmi Azham Shah
    • Muhammad Afiq Hanizar
    • Muhammad Hussain Ismail
    2018-11-30
    https://doi.org/10.14419/ijet.v7i4.26.22134
  • Bending strength, bone staple, stainless steel, titanium alloy.

  • Abstract

    This study compares bending behavior of metallic bone staples made with different metallic alloys; SS316L, CpTi and Ti40Nb. The staples were prepared by EDM wire cut in accordance with ASTM F564-10, standard specification and test methods for metallic bone staples. The materials of SS316L and CpTi were initially obtained from commercial rod, while the Ti40Nb alloy was manufactured by powder metallurgy (PM) process. Through this comparative study, development and feasibility of Ti40Nb, a β-rich TiNb alloy performance as a biomedical device specifically bone staple is studied. In the four point bending test, the data obtained for the metallic staple bending strength were 11.16±1.57 N/mm, 12.22±1.77 N/mm and 6.76±0.46 N/mm for SS316, CpTi and Ti40Nb, respectively. Only Ti40Nb experience failure whereas SS316 and CpTi bone staples suffers permanent deformation without failure.

     

     

  • References

    1. [1] Q. J. Hoon, M. H. Pelletier, C. Christou, K. A. Johnson, and W. R. Walsh, “Biomechanical evaluation of shape-memory alloy staples for internal fixation—an in vitro study,†J. Exp. Orthop., vol. 3, no. 1, (2016), p. 19.

      [2] A. F. Saleeb, B. Dhakal, and J. S. Owusu-Danquah, “Assessing the performance characteristics and clinical forces in simulated shape memory bone staple surgical procedure: The significance of SMA material model,†Comput. Biol. Med., vol. 62, (2015), pp. 185–195.

      [3] T. F. Smith, The Podiatry Institute Update Chapters : Chapter 41 - Tried and True Superhero of Bone Fixation. (2010).

      [4] Z. Lekston, D. Stroz, and M. J. Drusik-Pawlowska, “Preparation and characterization of nitinol bone staples for cranio-maxillofacial surgery,†J. Mater. Eng. Perform., vol. 21, no. 12, (2012), pp. 2650–2656.

      [5] T. A. Harris, “Emerging Concepts With Dynamic Compression Staples In Foot Surgery,†Pod. Today, vol. 30, no. 3, (2017), pp. 1–5.

      [6] M. H. Ismail, R. Goodall, H. a. Davies, and I. Todd, “Porous NiTi alloy by metal injection moulding/sintering of elemental powders: Effect of sintering temperature,†Mater. Lett., vol. 70, (2012), pp. 142–145.

      [7] M. I. Jamaludin, N. A. A. Kasim, N. H. M. Nor, and M. H. Ismail, “Development of porous Ti-6Al-4V Mix with palm stearin binder by metal injection molding technique,†Am. J. Appl. Sci., vol. 12, no. 10, (2015), pp. 742–751.

      [8] N. H. N. Elmi Azham Shah, M. Yahaya, M. Sulaiman, and M. H. Ismail, “a Metallurgical Overview of Ti – Based Alloy in Biomedical Applications,†J. Teknol., vol. 76, no. 7, (2015).

      [9] D. Kuroda, M. Niinomi, M. Morinaga, Y. Kato, and T. Yashiro, “Design and mechanical properties of new β type titanium alloys for implant materials,†Mater. Sci. Eng. A, vol. 243, no. 1–2, (1998), pp. 244–249.

      [10] P. Thomas et al., “Increased metal allergy in patients with failed metal-on-metal hip arthroplasty and peri-implant T-lymphocytic inflammation,†Allergy Eur. J. Allergy Clin. Immunol., vol. 64, no. 8, (2009), pp. 1157–1165.

      [11] B. Sharma, S. K. Vajpai, and K. Ameyama, “Microstructure and properties of beta Ti-Nb alloy prepared by powder metallurgy route using titanium hydride powder,†J. Alloys Compd., vol. 656, (2015), pp. 978–986.

      [12] M. Bönisch et al., “Thermal stability and latent heat of Nb–rich martensitic Ti-Nb alloys,†J. Alloys Compd., vol. 697, (2017), pp. 300–309.

      [13] D. Zhao, K. Chang, T. Ebel, H. Nie, R. Willumeit, and F. Pyczak, “Sintering behavior and mechanical properties of a metal injection molded Ti-Nb binary alloy as biomaterial,†J. Alloys Compd., vol. 640, (2015), pp. 393–400.

      [14] É. S. N. Lopes, C. A. F. Salvador, D. R. Andrade, A. Cremasco, K. N. Campo, and R. Caram, “Microstructure, Mechanical Properties, and Electrochemical Behavior of Ti-Nb-Fe Alloys Applied as Biomaterials,†Metall. Mater. Trans. A, vol. 47, no. 6, (2016), pp. 3213–3226.

      [15] M. Geetha, a. K. Singh, R. Asokamani, and a. K. Gogia, “Ti based biomaterials, the ultimate choice for orthopaedic implants - A review,†Prog. Mater. Sci., vol. 54, no. 3, (2009), pp. 397–425.

      [16] M. Long and H. J. Rack, “Titanium alloys in total joint replacement--a materials science perspective.,†Biomaterials, vol. 19, no. 18, (1998), pp. 1621–1639.

      [17] ASTM International, “Standard Specification and Test Methods for Metallic Bone Staples,†Astm F564-10(2015), vol. 03, no. Reapproved, (2015), pp. 1–18.

      [18] BioMedical Enterprises, “Speed Titan Datasheet,†San Antonio, TX, (2016).

      [19] M. Yahaya, S. Sahidin@Salehudin, M. Sulaiman, N. H. N. E. Azham Shah, and M. H. Ismail, “Microstructures and Mechanical Properties of Ti-Nb Alloy at Different Composition of Nb Produced via Powder Metallurgy Route,†Mater. Sci. Forum, vol. 863, (2016), pp. 14–18.

      [20] Wright Medical Group, “Charlotte TM claw TM Compression Locking Arthrodesis,†Memphis,TN, (2016).

  • Downloads

  • How to Cite

    Hidayatul Nadhirah Elmi Azham Shah, N., Afiq Hanizar, M., & Hussain Ismail, M. (2018). Comparative Study on Bending Strength of Metallic Bone Staple. International Journal of Engineering & Technology, 7(4.26), 40-44. https://doi.org/10.14419/ijet.v7i4.26.22134

    Received date: 2018-11-29

    Accepted date: 2018-11-29

    Published date: 2018-11-30