Tensile Property of Melt Mixing Co-Polypropylene with Waste Polymer at Different Composition Ratios

  • Authors

    • N. A. Sufian
    • A. Z. M. Rus
    • A. Shahrizan Syah
    • Farhana Hazwanee M. J
    • Noraini M
    • S. Aida I
    https://doi.org/10.14419/ijet.v7i3.28.23433
  • Co-polymer, Waste polymer, Injection moulding, tensile test, Stress-strain.
  • Abstract

    In order to implement economical way of managing unwanted substances, waste polymer (WP) can be recycled instead of throwing it away. It can be reused via "sink-float" technique and mixed with another binder like co-polypropylene (co-PP) to enhance the mechanical properties of the material. This is because co-PP is a bit softer but has better impact strength, much tougher and more durable than polypropylene (PP). Two materials underwent injection moulding with 170°C temperature to produce dog bone samples for tensile test. The test started with 10% up until 80% of WP content mixed with co-PP. Tensile test speed used for this experiment was 5mm/s. Stress vs. strain graph was obtained from the test and the modulus of elasticity was obtained by using the stress over strain formula. The stress versus strain result for the composite with WP is lower than that of co-PP, proving that WP is more brittle compared to the more elastic co-PP. Morphological analysis of surface structure based on Optical Microscope (OM) indicates that co-PP has smooth surface while WP has a rough surface.

     

     

  • References

    1. [1] K. Hamad, M. Kaseem, F. Deri. (2013). Recycling of waste from polymer materials: An overview of the recent works. Polymer Degradation and Stability 98(12), 2801-2812.

      [2] M. Pannirselvam, (2008). Design, development and characterization of polypropylene clay nanocomposites. PhD thesis, RMIT University.

      [3] Karian, H. (2003). Handbook of polypropylene and polypropylene composites, revised and expanded. CRC Press.

      [4] Wagner Jr, J. R. (2016). Multilayer flexible packaging. William Andrew.

      [5] Shubhra, Q. T., Alam, A. K. M. M., & Quaiyyum, M. A. (2013). Mechanical properties of polypropylene composites: A review. Journal of Thermoplastic Composite Materials 26(3), 362-391.

      [6] Jabarin, S. A. (1993). Orientation and properties of polypropylene. Journal of Reinforced Plastics and Composites 12(4), 480-488.

      [7] Maddah, H. A. (2016). Polypropylene as a promising plastic: A review. American Journal of Polymer Science 6(1), 1-11.

      [8] Paula, G. (2016). Polypropylene: Properties, uses and benefits. Nova Science Publishers.

      [9] Daniel, D. J., & Panneerselvam, K. (2017). Investigation on the effects of Cloisite 30B and copolymer (ethylene and butyl acrylate) reinforcement with polypropylene thermoplastic by melt intercalation method. Journal of Thermoplastic Composite Materials 2017, 1-22.

      [10] Caveda, S., Pérez, E., Blázquez-Blázquez, E., Peña, B., van Grieken, R., Suárez, I., & Benavente, R. (2017). Influence of structure on the properties of polypropylene copolymers and terpolymers. Polymer Testing 62, 23-32.

      [11] Hongjun, C., Xiaolie, L., Dezhu, M., Jianmin, W., & Hongsheng, T. (1999). Structure and properties of impact copolymer polypropylene. I. Chain structure. Journal of Applied Polymer Science 71(1), 93-101.

      [12] Chen, F., Shangguan, Y., Jiang, Y., Qiu, B., Luo, G., & Zheng, Q. (2015). Toughening with little rigidity loss and mechanism for modified polypropylene by polymer particles with core–shell structure. Polymer 65, 81-92.

      [13] Cheruthazhekatt, S., Pijpers, T. F., Harding, G. W., Mathot, V. B., & Pasch, H. (2012). Compositional analysis of an impact polypropylene copolymer by fast scanning DSC and FTIR of TREF-SEC cross-fractions. Macromolecules 45(15), 5866-5880.

      [14] Tang, C., Shi, B., Gao, W., Chen, F., & Cai, Y. (2007). Strength and mechanical behavior of short polypropylene fiber reinforced and cement stabilized clayey soil. Geotextiles and Geomembranes 25(3), 194-202.

      [15] Cui, J., & Forssberg, E. (2003). Mechanical recycling of waste electric and electronic equipment: A review. Journal of Hazardous Materials 99(3), 243-263.

      [16] Sasse, F., & Emig, G. (1998). Chemical recycling of polymer materials. Chemical Engineering and Technology: Industrial Chemistryâ€Plant Equipmentâ€Process Engineeringâ€Biotechnology 21(10), 777-789.

      [17] Webb, H. K., Arnott, J., Crawford, R. J., & Ivanova, E. P. (2012). Plastic degradation and its environmental implications with special reference to poly (ethylene terephthalate). Polymers 5(1), 1-18.

      [18] DomíNguez, F. N., & García-Morales, M. (2011). The use of waste polymers to modify bitumen. In Polymer Modified Bitumen. Cambridge: Woodhead Publishing, pp. 98-135.

      [19] Mastral, A. M., García, T., Callén, M. S., Navarro, M. V., & Galban, J. (2001). Assessment of phenanthrene removal from hot gas by porous carbons. Energy and Fuels 15(1), 1-7.

      [20] Mastral, A. M., Garcia, T., Callen, M. S., Lopez, J. M., Murillo, R., & Navarro, M. V. (2001). Effects of limestone on polycyclic aromatic hydrocarbon emissions during coal atmospheric fluidized bed combustion. Energy and Fuels 15(6), 1469-1474.

      [21] Mastral, A. M., Murillo, R., Navarro, M. V., Callen, M. S., & García, T. (2001). Assessment of schemes for the processing of organic residues from the interior car decoration industry. Industrial and Engineering Chemistry Research 40(4), 1119-1124.

      [22] Lin, Y. H., & Yang, M. H. (2007). Catalytic conversion of commingled polymer waste into chemicals and fuels over spent FCC commercial catalyst in a fluidised-bed reactor. Applied Catalysis B: Environmental 69(3-4), 145-153.

      [23] Singh, G., & Verma, A. (2017). A Brief Review on injection moulding manufacturing process. Materials Today: Proceedings 2(4), 1423-1433.

      [24] Reis, J. M. L., Pacheco, L. J., & da Costa Mattos, H. S. (2013). Tensile behavior of post-consumer recycled high-density polyethylene at different strain rates. Polymer Testing 32(2), 338-342.

      [25] Chow, T. S. (1991). Prediction of stress-strain relationships in polymer composites. Polymer 32(1), 29-33.

      [26] Kontou, E., & Farasoglou, P. (1998). Determination of the true stress–strain behaviour of polypropylene. Journal of Materials Science 33(1), 147-153.

      [27] Valenza, A., & La Mantia, F. P. (1987). Recycling of polymer waste: Part 1—Photo-oxidized polypropylene. Polymer Degradation and Stability 19(2), 135-145.

      [28] Turku, I., Keskisaari, A., Kärki, T., Puurtinen, A., & Marttila, P. (2017). Characterization of wood plastic composites manufactured from recycled plastic blends. Composite Structures 161, 469-476.

      [29] Ou, R., Xie, Y., Wolcott, M. P., Yuan, F., & Wang, Q. (2014). Effect of wood cell wall composition on the rheological properties of wood particle/high density polyethylene composites. Composites Science and Technology 93, 68-75.

  • Downloads

  • How to Cite

    A. Sufian, N., Z. M. Rus, A., Shahrizan Syah, A., Hazwanee M. J, F., M, N., & Aida I, S. (2018). Tensile Property of Melt Mixing Co-Polypropylene with Waste Polymer at Different Composition Ratios. International Journal of Engineering & Technology, 7(3.28), 261-265. https://doi.org/10.14419/ijet.v7i3.28.23433

    Received date: 2018-12-08

    Accepted date: 2018-12-08