Experimental and Analytical Study of Different Fiber Reinforced Composites with Damage
-
https://doi.org/10.14419/ijet.v7i3.10.25364
-
Composites, Experimental Tests, Damage, Repair, Crack -
Abstract
Composites are the materials which are majorly used in applications of aerospace, defense, transportation, communication, power, electronics, recreations porting and other commercial and consumer products. It is thus becoming more and more important that long term behavioral characteristics of the materials and structures are understood and implications of variety of flaws determined with respect to load conditions. This is to pay particular attention to fiber reinforced composites and its damage. The composites have fibers. Interwoven in orthogonal directions and cracks were introduced in different angles and composites coupons were undergone experimental procedures so that variation of tensile strength and stress strain curves are possible to study their effect on the composites. Different characteristics of damage on failure and remaining life were been clearly viewed by the result of non- linear finite element models tensile test were carried out using standard conditions
Â
Â
-
References
[1] R.J.a.Ehart,S.E.Stanzl-Tschegg,E.K.Tschegg “ crack face intrection and mixed mode fracture of wood composite during III loading â€.Engineering fractures Mechanics, 61 253-278,1998
[2] J.Chevalier,C.Olagnon,G.Fantozzi, “ Crack propagation and fatigue in zinconia – based composites †Elsevier Science Ltd. Composites: Part A 30525-530,1999
[3] Akira Kuraishi, Stephen W. Tsai, and Julie Wang, “ Material characterization of glass, carbon and hybrid fiber SCRIMP panels †SAND2002-3538 Unlimited Release Printed December 2002
[4] William A. Schulz, Donald G Myers, Tom N Singer, Peter G, Ifju Raphael T. Haftka, “Determination of esidual stress and thermal history for IM7/977-2 Composite laminatesâ€, Composite Science and Technology 65 2014_2024,2005
[5] Jane Maria Faulstich de Paiva. Sergio Mayer, Mirabel CerqueiraRezende “Comparison of tensile strength of different carbon Fabric reinforced epoxy composites†Materials Research.Vol.9, No.1,83-89.2006
[6] Dalbir Singh and A. Rajaraman “ Remaining Life Assessment of Damaged Reinforced Composites under Inelastic Material Behavior†ARPN journal of Engineering and Applied Science,Vol-8,April 2013
[7] S.Gasparyan. “ Determination of residual stresses in metallic composites†Journal of Materials Processing Technology 178 14_18,2006
P.K. Dash, D. Singh, “Shear characterization of woven carbon/epoxy composite under various adverse environments†STR Journal, Blackwell puplishing Ltd., Strain DO:10.1111/J.1475-1305.2010.00736.x,2010
-
Downloads
-
How to Cite
Sasikumar, R., Vinodh, S., Saravana Kumar, M., & Sabaree, M. (2018). Experimental and Analytical Study of Different Fiber Reinforced Composites with Damage. International Journal of Engineering & Technology, 7(3.10), 207-210. https://doi.org/10.14419/ijet.v7i3.10.25364Received date: 2019-01-04
Accepted date: 2019-01-04